Potential industrial utilization of pre-treated municipal solid waste incineration fly ash
No Thumbnail Available
Date
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
Description
Journal Article
This study sought to establish the effectiveness of water washing pre-treatment on the quality of municipal solid waste incineration (MSWI) fly ash (FA) for reuse and solidification or stabilization (S/S). Initial analysis of the FA sample shows that it did not meet the USEPA-1311 toxicity characteristic leaching procedure (TCLP) regulatory limits of 2011. As a result, a two-stage water washing process was carried out an attempt to improve the quality of the MSWI FA. After the washing pre-treatment, the heavy metals in the FA sample met the regulatory limits, thereby making it non-toxic for reuse or safe disposal. The leachate from the washing process also passed regulatory standards of China (GB 8978 – 1996) and the 2011 USEPA-1311. The washing process successfully removed more than 98% of each heavy metal under study. The process was excellent at removing cadmium (99.99%) and very good at removing the rest of the heavy metals. The 28-day compressive strength increased as the quantity of FA decreased. Also, all the heavy metals in the samples prepared with the pre-treated FA met the USEPA-1311 TCLP regulatory limit for reuse and safe disposal. The heavy metals leachability and compressive strength tests showed that the effect of cement-based S/S was largely influenced by its quantity in the samples. The highest compressive strength was attained by using 55% of the FA as replacement for cement. However, FA replacements of up 70% also yielded good results that met the 1989 USEPA standard of 0.34 MPa (50 psi)
This study sought to establish the effectiveness of water washing pre-treatment on the quality of municipal solid waste incineration (MSWI) fly ash (FA) for reuse and solidification or stabilization (S/S). Initial analysis of the FA sample shows that it did not meet the USEPA-1311 toxicity characteristic leaching procedure (TCLP) regulatory limits of 2011. As a result, a two-stage water washing process was carried out an attempt to improve the quality of the MSWI FA. After the washing pre-treatment, the heavy metals in the FA sample met the regulatory limits, thereby making it non-toxic for reuse or safe disposal. The leachate from the washing process also passed regulatory standards of China (GB 8978 – 1996) and the 2011 USEPA-1311. The washing process successfully removed more than 98% of each heavy metal under study. The process was excellent at removing cadmium (99.99%) and very good at removing the rest of the heavy metals. The 28-day compressive strength increased as the quantity of FA decreased. Also, all the heavy metals in the samples prepared with the pre-treated FA met the USEPA-1311 TCLP regulatory limit for reuse and safe disposal. The heavy metals leachability and compressive strength tests showed that the effect of cement-based S/S was largely influenced by its quantity in the samples. The highest compressive strength was attained by using 55% of the FA as replacement for cement. However, FA replacements of up 70% also yielded good results that met the 1989 USEPA standard of 0.34 MPa (50 psi)
Keywords
Fly ash, hazardous waste, heavy metal, municipal solid waste, reuse, solidification/stabilization